Whte Metal Models

Post

Posted
Rating:
#199496 (In Topic #11063)
Avatar
Full Member
It was the Dearne District Tramway that got me into trams, especially those English Electric four wheelers. My card efforts have been heading in that directions as there were no over the counter models available. No more, KW models now has a body model of siad tram. Not being one to repeat others efforts if I can help/affort it I was wondering about having a go.

However, I have never gone down the white metal route and was wondering if anyone ele has for trams. What is the best method of assembly an holding together. Traditionally it was solder but with modern adhesives I suspect life might be a bit easier. Bodies are £30 and BEC have a suitable chassis. Anyone any experience of white metal trams?

David

freelance model railways and tramways
index02
Online now: No Back to the top

Post

Posted
Rating:
#199497
Avatar
Full Member
Hi David,

While not trams, I've done a few white metal kits in the past using two part epoxy and superglue and it's a slow process to get good results, as the kits require a fair bit of preparation. I sill have a couple more loco kits in stock yet to build and will be trying the solder route this time, as it's quicker and they're supposed to stay stuck together longer! I will however practice with some smaller kits first and use low melt solder, as white metal kits still need a reasonable competency level and much patience to get the desired result.

It will be a good idea if you too can practice on something inexpensive to build up your confidence if you're not used to either kit building in general, or white metal kits in particular. In addition to the assembly, there can also be much preparation required prior to painting. However, with a little practice and taking plenty of time over everything, good results can be obtained.

Others here will have greater experience than me and I'm sure will offer further advice.

Good luck and chat soon,

Bill :)

Last edit: by Longchap


At 6'4'', Bill is a tall chap, then again, when horizontal he is rather long and people often used to trip over him! . . . and so a nickname was born :)
 
Online now: No Back to the top

Post

Posted
Rating:
#199498
Avatar
Full Member
I've also only done locos, in N gauge, a variable temperature soldering iron is a must, and also it must go down to 100C or less, white metal from different manufacturers does not always melt at the same temperature most melt around 150C but the Carr's lo melt solder is 70C so. Quite a few variable temp irons only go down to 150C which is too close to the borderline for my liking, a Weller WHS40LT is about as good as they get, but not cheap, this one is well below RRP and quite a bit below what I paid for mine.

Solder Station Weller Iron WHS40 Temperature Controlled 40W, 450°C

If you're looking for one after these have gone make sure it's the LT version, the normal WHS40 only goes down to 150C.

The only minor gripe I have with it is that the control is not calibrated in degrees, so you need to run tests with different melting point solders or a pyrometer and make your own marks.









Cheers MIKE
I'm like my avatar - a local ruin!
Online now: No Back to the top

Post

Posted
Rating:
#199500
Avatar
Inactive Member
I've done both railway stuff (locos, wagons, etc.) and also buses and lorries. Although I tend to solder the major bits together I use superglue for the detail parts. I did also put one of the old CCW O gauge white metal loco kits together using super glue and as far as I know it's still running and in one piece. The main thing to remember is to make sure everything fits well and is spotlessly clean before gluing together. I would suggest using one of the slower grabbing superglues to give you a few seconds fiddling time before it goes off.

I'm old, that's why I'm allowed to change my mind, when I can find it.

My Website: index
Online now: No Back to the top

Post

Posted
Rating:
#199506
Avatar
Full Member
Hi David,

No trams but plenty of white metal kits. Soldering is best, needs a low temp iron, and the correct solder and flux. I normally tack weld first (practice on some scrap pieces) then run the solder in the rest of the joint. The surfaces need to be freshly cleaned, grease-free, otherwise you will get a cold solder joint. 

I use an iron with a 15-60 Watt range set at 15-20 Watts and a tinned tip, never found the need for one of those expensive temperature controlled models as it's a different technique to soldering brass. I use low residue organic flux, gets the solder flowing beautifully and no clean-up necessary.

Keep away from 2-part epoxy, make a mistake and the parts will be in paint stripper for the next month while the epoxy dissolves. As soon as you clean the metal a thin oxide coat forms, that's what the epoxy will stick to unless it's done immediately after preparing the surfaces.

5-15 second gap-filling CAA works if the parts overlap and are cleaned immediately before gluing. and is a must for the detail bits. Just don't drop it, parts will fly everywhere.

Nigel

©Nigel C. Phillips
Online now: No Back to the top

Post

Posted
Rating:
#199508
Avatar
Full Member
Having built a few rail kits and a good many bus kits in white metal, I prefer the 5 minute epoxy glues (Araldite is my favourite). The bond is not as difficult to remove as the 24 hour stuff if you get it wrong, and it has a small amount of resilience to cushion the model should you drop it at any time (perish the thought, but this has been useful when buying pre-made kits from eBay and the like as it stands the rigours of postage much better than super glues).

Superglues, in my experience, don't work too well on edge joints with white metal because of the porous nature of the metal. This results in fairly brittle joints, When buying second-hand models for rebuilding or reconstruction, this has been an advantage in that by the time the model gets to me in the post, it has become a kit of parts again … ideal for my purposes as it is a much cheaper way of obtaining the kits than buying overpriced unmade examples!

Solder is also a good method but I have never been that competent at delicate soldering with low-melt solders, although I once repaired a badly cast tender side on a K's Q1 using normal melting point solder. I built up the layers slowly a little at a time until the missing bit of the casting was all filled, then filed it back to match the profile. No one told me you can't use normal solder with white metal, so I did it!

Sometimes, a combination of all of the above may be advisable. Superglue for a quick joint where there is danger of slippage, then epoxy or solder for strength.

Jeff Lynn,
Amateur layabout, Professional Lurker, Thread hijacker extraordinaire
Online now: No Back to the top

Post

Posted
Rating:
#199512
Avatar
Full Member
No experience with whote metal kits David - I've always read that it's not the easiest of materials to work with so have avoided it.

However, I do have some experience (a little) with BEC motor bogies and don't like them !!!  To me, they seem like a "blast from the past" - we've moved on from the old clunky 3 pole motor that's either "full on" or "off".  Not good news for trams I fear.  Try Halling of Austria.  More expensive, yes, but (IMHO), light years ahead of BEC.

I'm usually disappointed by the lack of scale speed on tram layouts.  Most seem to run at a scale 200 mph and catapult the poor passengers into either the back or front windows depending on whether the tram is starting off or stopping.  Halling motors are far more controllable.

'Petermac
Online now: No Back to the top

Post

Posted
Rating:
#199523
Guest user
Hi David I did some repairs to a few white metal n gauge farm vehicles (wheels/axles broken off etc) and used original superglue with no problems apart from sticking my fingers to various bits
Back to the top

Post

Posted
Rating:
#199536
Avatar
Full Member
Hi David,
Srman brought up the issue of porosity. If the molten metal was degassed (which it should have been but you are at the mercy of the caster) and was cast in a centrifuge porosity is not an issue, especially for slow curing CAA which likes as much surface as possible. You do need an overlapping flange  which hopefully was designed in. If not solder it. 
My experience with 5 minute epoxy is that the adhesion is questionable unless it is used immediately the metal is cleaned. It gets as hard as regular epoxy after a week or so anyway.
It's worthwhile enquiring what the white metal melt temperature is. It can range considerably depending on the alloy composition. I would use a big, slow rpm high torque motor and use it to drive bogies with high ratio gearing. Hollywood Foundry Lowboy is worth having a look at. 
Nigel

©Nigel C. Phillips
Online now: No Back to the top

Post

Posted
Rating:
#199539
Avatar
Full Member
It's worthwhile enquiring what the white metal melt temperature is. It  can range considerably depending on the alloy composition.

I did a Google for white metal melting point, evidently it can be as low as 135C up to about 350C which is why I would not like to take a chance wiyh an iron that only goes down to 150C; if possible try and find a spot on the model to test that will not be  noticed or which can be easily filled if you do melt a bit. I usually fit brass buffers in place of any supplied white metal ones, so a buffer is a handy test  item.

I prefer 70C lo melt solder, which is well below white metal melting point so an iron with a min 100C  is fine.

Cheers MIKE
I'm like my avatar - a local ruin!
Online now: No Back to the top

Post

Posted
Rating:
#199545
Avatar
Full Member
I'm with Mike, 100°C no tinning required or even 70°C solder (ideal for putting brass bits on after tinning).

I've had kits where my iron set at 15 Watts melted the castings (OK if tack welding) and others where 25 Watts was perfectly fine. All that white metal acts as a very efficient heat sink, the idea with the solder is to use the iron to get it to follow the flux, not to heat all the metal so that the solder melts and flows in. Hence mu use of organic flux. Adding brass bits is different, heat the brass to melt the tinned solder.

Nigel

©Nigel C. Phillips
Online now: No Back to the top

Post

Posted
Rating:
#199615
Avatar
Full Member
Thanks for the various comments. On trhe subject of soldering I am wondering if it is more like welding on cast models. If the metal itself melts at such low temperatures is soldering actually possible?

Metallurgy was never my best subject but I remember the diagram that showed the lowest melting point for alloys and it was very low for some. One even below boiling point of water, used at one time by plumbers to aid bending of pipes.

I think BEC bogies just use a standard model electric motor much the same as everyone else. They are significantly cheaper, at least in the UK, that some of the stuff on offer.

I would assume glues are the way to go. If they are good enough to hold planes and cars together then I suspect they are fine for a model. From the comments it looks as though simple assembly jigs and fixtures help while the glue sets.

There is a new product on the DIY market called SUGRU. basically a room temperature hardening rubber. Check out the site, sugru.com I think. I have tried it out on some models and it seems to work. It certainly works as a general repair product.

Thanks again.

David

PS further observations always welcome.

Just remembered. SUGRU application below.


freelance model railways and tramways
index02
Online now: No Back to the top

Post

Posted
Rating:
#199617
Avatar
Full Member
If you look back to my post #10 on Tuesday, White metal alloy lowest melting point 135C, (some alloys though can be as high as 350C) low melt solder 70C, soldering iron at min setting 100C, that sounds like soldering to me, an iron with a minimum setting of 150C could well be welding if used on 135C white metal!

Cheers MIKE
I'm like my avatar - a local ruin!
Online now: No Back to the top

Post

Posted
Rating:
#199648
Avatar
Full Member
I think you are right. From my limited knowledge of the normal casting metals they have melting points well above normal soldering temparatures. Really low melting point metals are probably for specialist applications and prices to suit.

White metal casting is one technique I have always fancied having a go at. Taranti sell a started kit and Irish model soilder companies stuff is widely available. Cannot remember the name but many, many years ago on a motorcycle tour of Ireland we are riding down this road out in the country when a sign appears for the model soilder company. Prince August (Hoobies Catalogue) , basically a shop attached to the factory.

I do not know if general purpose 3D printers have the facility yet, but one application of 3D printing is to print complex forms with casting wax and then use the model to make a lost wax casting mould.

David

freelance model railways and tramways
index02
Online now: No Back to the top

Post

Posted
Rating:
#199652
Avatar
Full Member
Hi David,
You're a braver man than I. Just make sure you clear it with the authorities, they look askance these days on backyard foundries. Plus you'll probably need the scrubbers to limit environmental pollution from all those metals. I looked into this a few years ago, stopped after it got past 5 figures. Resin casting is a lot easier, but poses another set of environmental and health/safety issues. Brass etches in comparison are easy, do the artwork and send it off. First one is expensive, the rest are not. Not good for curvy bits though. 
One of the reasons solder is getting more difficult to find (the low melt types) is that manufacturing facilities are becoming fewer. 
Nigel 

©Nigel C. Phillips
Online now: No Back to the top

Post

Posted
Rating:
#199657
Avatar
Full Member
All you need to know about solder and soldering including  catalogue of solder in bar, strip and reels. solder cream/paint and fluxes.

http://www.finescale.org.uk/index.php?route=product/category&path=446_453

http://www.finescale.org.uk/index.php?route=product/category&path=446_452



Cheers MIKE
I'm like my avatar - a local ruin!
Online now: No Back to the top

Post

Posted
Rating:
#199662
Avatar
Full Member
Good reading material, but as Pete from C+L points out, it's not getting easier re solder supplies. I only use one flux for brass and white metal, really good solder helps a lot. I rarely solder up steel (and rare indeed are steel parts in kits). If the metal faces are freshly cleaned and grease free really aggressive fluxes are not necessary. MAZAC I keep away from, easier to drill and tap. 
Nigel

©Nigel C. Phillips
Online now: No Back to the top

Post

Posted
Rating:
#199669
Avatar
Full Member
Surfing the net and found this:



No fiddly soldering iron here.

freelance model railways and tramways
index02
Online now: No Back to the top

Post

Posted
Rating:
#199670
Avatar
Full Member
And on the subject of the home foundry:

White Metal Casting | Toy Soldier Miniatures | Themed Chess Sets

adaptable to model railways i think.

freelance model railways and tramways
index02
Online now: No Back to the top

Post

Posted
Rating:
#199672
Avatar
Full Member

freelance model railways and tramways
index02
Online now: No Back to the top
1 guest and 0 members have just viewed this.